In order to improve the magnetic properties of Nd-Fe-B/ α-Fe nanocrystalline permanent magnets, the effect of heat treatment on magnetic properties of Nd_8Fe_ 77B_6Co_8Nb_1 nanocomposite magnetic material prepared by rapid quenching and crystallization heat treatment was studied.

The fatigue life-spans of specimens after dehydrogenization heat treatment and crystallization heat treatment are all decreased observably, which is caused by the tension internal stress.

经过除氢热处理和晶化热处理的试样的疲劳寿命，与基底试样和镀态试样相比都显著降低，而热处理后试样疲劳强度的降低是由于镀层的内应力引起的。

Compared with one-step crystallization heat treatment, the two-step crystallization heat treatment is helpful to improve the mechanical properties of glass-ceramics.

与一步法热处理相比，采用两步晶化热处理有利于提高微晶玻璃的力学性能。

Microstructure observation of γ-TiAl after subsequent heat treatment shows that: after the crystallization heat treatment, recrystallization occurs in the surface layer, and the center microstructure maintains the prior equiaxed grains as that before cold deformation.

对喷丸后的Q235钢进行热处理和显微组织观察，结果表明：经过在结晶热处理，表层晶粒发生再结晶，而心部组织保持为冷变形前细小的等轴晶形态。

The results showed that the crystallization heat of PA6 decreased when PA6 was blended with POE. In the presence of compatibilizer,γ crystal and crystal rate of PA6 in TPE decreased.

结果表明，POE降低了TPE中PA6的结晶热，相容剂的加入使TPE中PA6的γ结晶减少以及降低了PA6的结晶速度。

When the glass is annealed at 750 ℃ prior to crystallizing treatment, bulk crystallization is preferable and fish-bone shaped crystals and the strip-liked texture are appeared in the samples with 5.0% and 15% ZnO respectively.

玻璃先在750℃低温退火处理有利于晶体的整体析出，晶体形态由ZnO为5%时的鱼骨状变为15%时的条带状组织。

The crystallization in ultrathin polymer films depends strongly on film thickness ( D), particularly those with D < 20 nm exhibit a great deviation from bulk crystallization both in crystalline morphology and crystallization kinetics.

聚合物超薄膜结晶与膜厚（D）有很强的相关性，尤其是D<20nm的薄膜在结晶形貌和结晶动力学方面与本体结晶差别很大。

The melting point, crystallinity, bulk crystallization rate and crystallization capability of the blends decreased with the increase of the content of PEI;

随PEI含量的增加，共混体系的熔点、结晶度、整体结晶速率和结晶能力均降低；

Crystallite Size and Lattice Distortion of TiC from X-ray Diffraction Line Profile Analysis

用XRD线形分析法表征TiC粉体中的镶嵌尺寸与晶格畸变

Determination of crystallite size and strain by X-ray powder

晶粒尺寸和应变的X射线粉末衍射法测定

The higher the calcination temperature, the larger the crystallite size.

焙烧温度越高，晶粒尺寸越大；

The results show that the sample with larger crystallite size has higher resistance.

结果表明结晶尺寸大的样品电荷传递电阻较大。

A study on appraisal method of crystallite size for nanometre materials

纳米材料晶粒鉴定方法的研究

Method of determination of the crystallite size distribution of active component of catalyst and Its Applications

催化剂活性组分晶粒大小分布的测定方法及应用

Computer Application in the Calculation of Crystallite Size

计算机在晶粒大小计算中的应用

Biological systems are able to generate crystalline materials with complex morphologies and specific functions via the processes of biomineralization and these processes are elaborately controlled by some biomacromolecules.

生物体能够在生物大分子的精确控制下，通过生物矿化过程合成具有特殊形貌和功能的生物矿物。

A main focus of the review is to elucidate the emplacement history of the high-grade Greater Himalayan Crystalline Complex ( GHC) that occupies the core of the orogen.

文章的主要目的是阐明占据造山带核部的大喜马拉雅结晶岩带（GHC）的侵位历史。

The crystalline grain size and the distortion of interfacial atoms have great influence on the D.

晶界原子畸变和晶粒尺寸对纳米体系的交流电导有重要的影响。

Study on Kinetics of Crystalline Grain Growth of Cu-Mn Complex Oxides Nanometer Powder Precursor

纳米铜锰复合氧化物前驱物晶粒生长动力学研究

With continuous ball grinding, the powder particle and crystalline grain gradually decreased.

球磨继续进行，合金化的粉末和晶粒不断细化。

The Control and Influence on Engine Turbine Blade Property of Crystalline Grain Quantity

晶粒度对发动机涡轮叶片性能的影响及其控制