acrylate的例句大全

The self-crosslinking acrylate printing adhesive was synthesized by emulsion polymerization.

采用乳液聚合法合成自 交联型 丙烯酸酯类印花粘合剂.

A non-formaldehyde self-cross-linking acrylate binder has been prepared by seed emulsion polymerization.

采用种子乳液聚合的方法,制备了一种无醛自交联丙烯酸酯印花粘合剂.

Reversed-phase precipitation; gas chromatography; methanol; residual monomer; silicone acrylate resin.

反相 沉淀法; 气相色谱法; 甲醇; 残余单体; 硅丙树脂.

ACR is a copolymer of methyl methacrylate with acrylate.

ACR是一种甲基丙烯酸甲酯与丙烯酸酯类的共聚物.

Octadecyl acrylate was synthesized with acrylic acid and octadecanol as raw materials.

以丙烯酸和十八醇为原料合成丙烯酸十八酯.

Acrylate, DDBSA and DMF were used to react under a two stage.

丙烯酸盐, DDBSA和二甲基甲酰胺之间的反应常常分二个阶段.

The acrylate oilabsorbing resin had higher rate of oilabsorbing.

采用该方法合成的丙烯酸酯类吸油树脂具有较高的吸油率.

The influences of silicon on organosilicon-modified acrylate emulsion were also discussed.

论述了硅对有机硅改性丙烯酸酯乳液的影响.

The degraded starch and acrylamide-butyl acrylate copolymer have been produced.

本文制得了异相酸降解淀粉和丙烯酰胺 — 丙烯酸丁酯共聚物.

The commonly-used materials of IOLs include polymethylmethacrylate ( PMMA ) , silicone, hydrogel and acrylate.

目前临床常用的人工晶状体的合成材料包括聚甲基丙烯酸甲酯(PMMA ) 、 硅凝胶(silicone) 、 水凝胶 ( hydrogel)和丙烯酸酯(acrylate).

Epoxy acrylate was synthesised by reacting epoxy resin with acrylic acid.

用丙烯酸和环氧树脂合成了丙烯酸环氧酯.

The styrene acrylate emulsion is prepared through the emulsion polymerization.

采用乳液聚合法制备环氧树脂改性苯乙烯-丙烯酸酯乳液.

An acrylate modified epoxy emulsion was prepared by compound emulsion polymerization techniques.

采用复合乳化剂聚合工艺,制得丙烯酸酯类改性环氧树脂乳液.

Meanwhile , fluorinated acrylate latexes performed better based on present experimental parameters.

三种材料中, 含氟丙烯酸酯共聚物乳液的性能相对比较好.

The effect of butyl acrylate ( BA ) dosage on adhesive was investigated.

研究了 BA 用量对胶粘剂性能的影响.

The self-crosslinking acrylate latex contained functional monomer DAAM 、 acrylamide and NMA through pre-emulsification polymerization process was prepared.

通过预乳化乳液聚合工艺，合成了含官能团单体双丙酮丙烯酰胺（DAAM）、丙烯酰胺、N-甲基丙烯酰胺（NMA）的自交联丙烯酸酯乳液。

A kind of novel PU and poly ( acrylate-co-methyl methacrylate) s with nonlinear optical conjugated group were synthesized. Their properties were studied.

本论文合成了一类含非线性生色团的长侧链的聚氨酯和一类聚丙烯酸酯及其与甲基丙烯酸甲酯的共聚物，并对它们的非线性光学性能进行了研究。

The initiation of the polymer immobilized initiator was investigated through the polymerization of methyl acrylate.

并研究了此引发剂引发丙烯酸甲酯的聚合反应.

Acrylate copolymerized emulsions of different structure and different formulas were synthesized. Polymer architectural waterproof coating and polymer cement waterproof coating were prepared. Their relevant properties were tested and several factors influencing performance were discussed.

合成了不同结构、不同配方的丙烯酸酯共聚乳液，配制了聚合物建筑防水涂料及聚合物水泥防水涂料，并进行了相关性能测试，讨论了影响性能的若干因素。

Methyl 3-methoxypropionate ( MMP ) was prepared from methanol and methyl acrylate ( MA ) using sodium methoxide as catalyst.

以甲醇和丙烯酸甲酯 ( MA ) 为原料,甲醇钠为催化剂,合成了 3- 甲氧基丙酸甲酯 ( MMP ).