annealed的例句大全

The martensitic transformation of retained austenite particles in an intercritically annealed low-alloy steel has been studied using the acoustic emission technique.

用声发射法研究了一种低合金钢于双相区热处理所得残余奥氏体的马氏体相变。

Study on Structure and Texture of Hot-Galvanized Layer of Cold-Rolled Sheet and Cold-Rolled Annealed Sheet Using IF Steel

IF钢冷轧板和冷轧退火板热镀锌层组织和织构的研究

The market demanding for bright annealed stainless steel sheet in China was predicted, the technical purpose and equipment requirement for the vertical bright annealing furnace were analyzed. Some key issues were pointed out which must be paid special attention to during construction of vertical bright annealing furnace.

预测我国不锈钢光亮退火板市场需求，分析立式光亮退火炉的工艺目的和设备要求，指出建造立式光亮退火炉需特别注意的问题。

The results show that there are four kinds of carbides in annealed state of the steel, and major portion of quenched martensite is lath-like martensite.

结果表明，该钢退火状态存在四种类型碳化物，淬火组织以板条马氏作为主。

Effect of Normalizing Temperature on Structure and Magnetic Properties of Annealed Non-Oriented Electric Steel

热轧板常化温度对冷轧无取向电工钢退火组织和磁性能的影响

The grain boundary character distributions in annealed 304 stainless steel at high and low temperature after slight cold-rolling

小形变冷轧304不锈钢高温和低温退火晶界特征分布研究

The best performance of millimicron surface layer can be obtained when the composite material is molded under shaping pressure 1.5 GPa and annealed at 350 t, whose hardness is up to around 290.

压强为1.5GPa压制成型的复合材料，经350℃退火可获得最佳性能的纳米表面层，显微硬度值可达到290左右。

Effect of Cold Deformation Rate and Heating Rate on Grain Size Distribution of Batch Annealed IF Steel

冷形变量和加热速率对IF钢罩式退火再结晶晶粒尺寸分布的影响

The ductile-embrittlement transition temperature of vermicular graphite cast iron increased with increasing phosphorus content both in the as-cast and annealed condition.

蠕铁的韧性&脆性转变温度铸态和退火态均随磷含量的增加而升高。

The results show that, after machining there is no difference about deformation between annealed casting and the one got from slow cooling process in sand mold.

结果表明，铸件在砂型中缓冷和去应力退火再经机加工后两者产生的变形量差异并不明显；

When the glass is annealed at 750 ℃ prior to crystallizing treatment, bulk crystallization is preferable and fish-bone shaped crystals and the strip-liked texture are appeared in the samples with 5.0% and 15% ZnO respectively.

玻璃先在750℃低温退火处理有利于晶体的整体析出，晶体形态由ZnO为5%时的鱼骨状变为15%时的条带状组织。

Used annealed paving blocks.

使用韧化的铺地块料。

Precipitation of oxygen and carbon in buk dislocation-free CZ Si annealed at450 ℃, 700 ℃ and 1050 ℃ has been studied using infrared absorption, X-ray topography, X-ray anomalous transmission, AES and HVTEM.

利用红外吸收、x射线形貌照相、x射线反常透射、俄歇电子能谱和高压透射电子显微镜研究了在450℃、700℃和1050℃热处理后无位错CZ-Si单晶中的氧、碳沉淀。

While annealed in the atmosphere, nano-crystalline LaF _ 3 was oxidized over 500 � � C.

在大气中退火温度超过500℃时, 纳米LaF_3块体会被氧化.

Above this point the hardness can be increased only slightly, because steels above the eutectoid point are made up entirely of pearlite and cementite in the annealed state.

高于此点，由于超过共析点钢完全由珠光体和退火状态的渗碳体组成，硬度增加并不多。

The thesis have systematically investigated the structural and transport properties of as-quenched and annealed Co xCu 100-x ( 5 ≤ X ≤ 30) granular alloys prepared by melt spinning.

系统研究了用快淬制备的铸态和退火处理后的颗粒合金膜CoxCu100-x（5≤X≤30）的结构及磁电阻性能。

DZ formed in the sample that annealed in nitrogen atmosphere.

经历氮气氛预处理的辐照样品中有一定宽度的清洁区形成。

XRD structural analysis shows that peak intensity of the annealed sample is greater than that of the unannealed one which demonstrated an increase of crystallinity.

XRD结构分析显示，退火后薄膜样品的峰值强度大于未退火样品的强度，说明样品结晶度增强。

The experimental results indicated that the film resistivity of the sample annealed was reduced significantly and only one3.17 of the unannealed.

实验结果表明：退火后样品的薄膜电阻率显著减小，是未退火样品薄膜电阻率的3.17分之一；

The Positron lifetime spectra of unannealed and annealed Ni-coats, electro-plated from the four typical baths, have been measured.

测量了四种典型镍镀层的采透火和退火试样的正电子湮没寿命谱。