The brittleness of brazed seam for nickel-base brazing filler metals is always paid close attention.

镍基 钎料的钎缝脆性问题,一直是人们关注的研究课题.

The theoretical calculation of brazed rate based on C-scan image is described.

利用超声无损检测C扫描图像,可以反应钎焊缺陷及其分布特征,并自动计算出钎着率.

Local fusion deformation occurred after the product antenna combination was brazed.

某产品天线组合钎焊后,局部发生熔化变形现象.

Assemble parts to be brazed.

组装准备铜焊的部件.

In this paper, Be and HR-1 stainless steel were bonded by brazed and diffusion bonded.

另一方面利用有限元方法模拟了铍与HR -1 不锈钢扩散焊区的浓度分布,模拟结果对合理制定工艺具有指导意义.

Radio frequency ultrasonic technique for metal brazed high-density honeycomb structures and defect recognition are described.

利用射频超声技术检测大密度金属钎焊蜂窝构件及缺陷识别技术.

Grinding performance of the brazed wheel in surface grinding of cemented carbide is studied.

以硬质合金为加工对象,研究了该砂轮的磨削性能.

In this paper, each forming operation during quadruple-wall curly brazed tubes'forming processes was summarized.

综合阐述了四层卷焊管成型过程中的各技术环节.

Effect of Specimen Size on the Residual Stress of Al_2O_3 and Nb Brazed Joint

试样尺寸对Al2O3陶瓷/Nb钎焊接头应力场分布的影响

Thus, the properties and microstructure of copper brazed double-walled steel tube made of CCSS also come up to that of the exotic products.

并且用其制成的双层卷焊钢管组织优良、性能符合标准要求，达到了国外同类产品水平。

The alloy element action and brazed seam structure are analyzed.

分析了钎料各合金元素的作用及钎缝组织。

Cut through the brazed seam on the connection to the side section with the parting grinder.

用分离打磨机切断连接到侧面部件的铜焊缝。

Further research shows that element Mg in 6063 is the main cause making the flux ineffective and the quality of brazed seam degraded.

进一步的研究指出：6063铝合金中的合金元素Mg是使钎剂失效和恶化钎缝质量的主要原因。

The results suggest the joint is not ideal if the Cu layer is too thin or too thick, and it is very important for existing some eutectic substance in brazed seam.

研究表明，Cu层的厚度太薄或者太厚，其连接效果都很不理想，同时在Al合金与Cu中间层接触反应钎焊中，钎缝区存在适当的液相对于提高接头强度是至关重要的。

The simulation mentioned above was confirmed by series experiments, and the proper thickness of the brazed seam is 50~ 80 μ m for the CRB joint of Al with Si as an interlayer.

在试验证明FEM计算结果的可靠性的基础上，给出了Si为中间层进行LF21铝合金接触反应钎焊时，其合适的钎缝宽度范围是50～80μm。

Cracking analysis of brazed phosphorus deoxidized copper tube

磷脱氧铜管焊接漏气失效分析

Study on effect of brazing temperature on wear properties of brazed WC coatings

钎焊温度对WC金属布钎焊耐磨层性能研究

The Influence of Brazing Metal on Residual Stresses in Brazed Joints of Ceramic-metal

钎料对金属/陶瓷钎焊接头残余应力的影响

The brazing-ability and quality of brazed seam of 6063 aluminum alloy brazed by Al-Si eutectic filler metal and QF flux is discussed by means of test of spread-ability and test of T joint.

本文用平百铺展试验和T型接头试验，研究了6063铝合金采用AI－St钎料和氟化物钎剂（QF钎剂）钎焊时的钎焊性和钎缝质量。

Microstructure of Brazed Joint of Bilayer Ceramic Composite and Steel

双层陶瓷复合材料与钢钎焊接头界面的微观组织结构