calcined的例句大全

The lattice parameters of calcined coke and foreign needle coke were similar, true density and ash content reached the new Japanese cosmetic company standards.

所制备的煅后焦的晶格参数与国外针状焦相近，真密度、灰分含量等性能均达到日本新日化公司标准。

Based on the experimental results, the interaction mechanism of the calcined coke grain and the binder was proposed with the hot binding and hot pressing process.

在实验基础上，阐明了粘结剂与骨料颗粒在热混捏与热压过程中相互作用原理。

The bulk graphite was prepared from starting materials of calcined coke and coal-tar pitch by the hot-pressing process.

以煅烧石油焦为基本填料，煤沥青为粘结剂，采用热压工艺制备石墨制品。

Clean Production Project for Calcined Coke Produced from Rotaty Oven

回转窑煅烧石油焦清洁生产方案研究

The influence of the real density of calcined coke on the bulk density of green electrodes

煅后焦真密度对生坯电极体积密度的影响

Effect of Graphite/ Calcined Coke on Friction Performance of Brake Pad

石墨/煅后焦对合成闸瓦试样摩擦性能的影响

An applied experiment of petro coke residue slurry was carried in a rotary kiln, we carry on systematic examination to the calcined alumina quality and waste gas of kiln tail etc.

在回转窑上进行了油焦浆应用试验，对高温氧化铝质量和窑尾废气等进行了系统检测。

The research shows the completive temperature of mullitization and the increment of mullite at different temperature range varies between the calcined bauxite and fused corundum which exist with kyanite.

研究表明兰晶石和矾土熟料与和电熔刚玉共存时材料中莫来石化完成温度和不同温度阶段莫来石的增量不同；

Under laboratory conditions, after calcined at the temperature of 700 ℃, red-mud is mixed with cement to produce a special kind of concrete, with which the standard concrete is compared in terms of breaking and stress intensity.

在实验室条件下，对赤泥进行700℃的煅烧处理，并利用其制取水泥赤泥混凝土，与基准混凝土的抗折、抗压强度进行对比。

In order to reduce the operation cost, a small dynamic test was done with the simulation of the operation conditions of the aeration basin, and calcined soda is being replaced by limewater.

为了降低运行成本，采用小型动态实验，模拟曝气池的运行条件，将石灰水代替纯碱以中和水质。

The colloid ed alumina hydroxide was prepared by precipitation using PEG as dispersing agent. Then the colloid was calcined at 800~ 1100 ℃/ 2h to get the nano powder of alumine.

以不同聚合度的聚乙二醇（PEG）为分散剂，采用沉淀法制备氢氧化铝胶体，胶体经800~1100℃高温煅烧得到纳米氧化铝粉体。

Effect of calcined anhydrite on Portland cement

煅烧硬石膏对硅酸盐水泥水化过程的影响

Through the examination of the sample's physical nature and hydration and the analysis of its hydration mechanism, it revealed that calcined phosphogypsum, slag, clinker, and chemical activators in a certain mixing ratio are ground finely to make the anhydrite cement with higher compression.

通过对样品的物理性能和水化产物的检测以及水化机理的分析表明：将高温煅烧磷石膏、矿渣、熟料和激发剂按一定的比例混合磨细可以制备出高强的硬石膏水泥。