corrosion的例句大全

Preferential corrosion cracking at or along the grain boundaries of a metal.

优先腐裂或沿着金属晶界发生的腐蚀.

Stress corrosion cracking in which the cracking occurs along grain boundaries.

沿着晶界发生的应力腐蚀开裂.

It is shown that the surface cracking is caused by the stress corrosion cracking.

结果表明,该表面开裂为应力腐蚀开裂.

Its shortcomings are mainly low structural stability, low low-frequency fatigue strength and stress corrosion cracking.

其缺点是组织稳定性不好 、 低频疲劳强度低、有应力腐蚀开裂倾向.

The reason, influence coefficient and control measure of the corrosion cracking were disserted in this article.

本文详细论述了不锈钢波形膨胀节腐蚀破裂的原因 、 影响因素及控制措施.

The results show that the fibre orientation affects on the stress corrosion cracking of GRP seriously.

结果表明,纤维取向对玻璃纤维增强塑料的应力腐蚀行为有很大影响.

This offers a practical e example that chlorine ion caused stress corrosion cracking of brass.

为氯离子引起黄铜应力腐蚀开裂提供了实例.

It also has a considerable resistance to corrosion by air and by many corrosive chemicals.

铝还有相当高的抗大气和许多化学药剂腐蚀的能力.

This is confirmed by SEM that it is caused by corrosion fatigue.

经扫描电镜断口分析确认,是腐蚀疲劳所致.

Some directional points are made in corrosion fatigue reliability of a structure.

对结构腐蚀疲劳可靠性做了方向性提示.

So, the sucker rod's main failure modes are fatigue fracture and corrosion fatigue crack.

因此, 抽油杆的主要失效形式为疲劳断裂和腐蚀疲劳断裂.

It has small drainage resistance, high anti-press strength, corrosion proof etc. advantages.

具有排水阻力小, 抗压强度高, 耐腐蚀等优点.

We choose the high quality and corrosion-proof steel as mould material.

模具材料选用高光洁,耐磨损的钢材制造.

Usage: It is a corrosion-proof scale preventative agent of superior effect for industrial cooling water system.

用途: 作为工业循环冷却水系统的阻垢缓蚀,其效果非常优异.

The shell is formed up of engineering plastic with properties of impact-with standing and corrosion-proof.

外壳采用工程塑料成形,具有较好抗冲击能力和 防腐蚀 能力.

Type I: Made of engineering plastic, corrosion-proof and-proof, it is used as leading device-increased shell.

型: 采用工程塑料压制而成, 具有较强的防腐和防水性能, 适用于增安型外壳中作引入装置用.

The corrosion test showed that such glass flakes contained paint could be adopted in different applications.

介绍了玻璃鳞片防蚀涂料的研制和应用.

Engineers need an understanding of the mechanical strength and corrosion resistance of various materials.

工程师需要了解各种材料的机械强度和耐腐蚀的能力.

Corrosion resistance of the product shall not be impaired by the marking.

产品的抗腐蚀性不会因为做标记而变差.

Gates are available, 316 or 317 steel for corrosion resistance.

316或317不锈钢闸板具有很好的耐腐蚀性能.