Cordierite-Mullite Board: It is made by high sintering cordierite and mullite together.

堇青石 — 莫来石棚板: 是以堇青石,莫来石两种材料混合成型,经高温烧结而成.

Mullite particles was synthesized by hydrothermal crystallization from kaolinite in coal measures.

以煤系高岭岩为原料,采用水热晶化法合成超细莫来石粉.

The experimental results show that factors above affect the rheology of mullite slurry significantly.

结果表明:上述因素对莫来石泥浆流变性能有显著的影响.

A fibre reinforced mullite insulating material has been developed under simple processing condition.

引入耐火纤维,在相对简单的工艺条件下研制了纤维增强莫来石隔热材料.

The substructure and the fracture process of mullite ceramics were studied by TEM and SEM.

用透射电镜和扫描电镜研究了莫来石陶瓷的亚结构特征和断裂过程.

Finally, the continuous mullite fibers with little porosity are prepared.

最终可以得到有较低孔隙率的莫来石连续纤维.

The reaction-sintering process and microstructure of mullite-zirconia composites sintered and reacted in-situ were investigated.

研究了用锆英石和工业氧化铝合成锆莫来石材料的反应烧结过程和显微结构.

Micropowder of mullite is manufactured by gap mill.

采用环缝磨制备了莫来石微粉.

Major phases of mullite composite nanocrystalline was synthesized by hydrothermal crystallization method.

以天然矿为原料,用水热法制备了主晶相为莫来石复合纳米晶.

ZrO 2-mullite compound powders were prepared from zircon in molten salt medium.

以锆英石为原料,采用熔盐合成法制备出了氧化锆 - 莫来石复合粉体.

Zirconia Toughened Mullite ( ZTM ) Ceramics is one of finest Performance high temperature structure ceramics.

氧化锆增韧莫来石 ( ZTM ) 是优良的高温结构陶瓷材料.

The properties of corundum-mullite-zirconia grogs made by reaction-sintering process and their carbon-bonded materials have been investigated.

研究了 反应烧结 制备的锆刚玉莫来石系熟料及其碳结合材料的性能.

Burned Zr-mullite bricks are new product developed by us.

烧结锆莫来石砖是我厂开发的新产品,填补国内空白.

The XRD result shows that the main crystalline phase of the ceramic is mullite.

射线衍射分析结果表明,材料的主晶相为莫来石.

Used for corundum bricks, mullite bricks, silicate bricks masonry in blast furnaces, hot air stoves.

用于高炉 、 热风炉砌筑刚玉砖、莫来石砖 、 硅线石砖 、 低蠕变高铝砖.

Transparent mullite ceramic film was prepared by Sol Gel.

采用溶胶－凝胶（Sol－Gel）工艺合成了莫来石透明陶瓷薄膜。

Study of Calcining Entire? Cast Furnace Lid Made with Mullite? Fly Ash

莫来石&粉煤灰整体浇注焙烧炉盖的研究应用

Study on Principal Crystalline Phase of Mullite Ceramics with Low Cost

低成本莫来石主晶相陶瓷的研究

After sintered in 1600 ℃, nearly dense mullite with fine crystalline particle was obtained.

试样在1600℃烧结得到接近致密、晶粒尺寸均匀、细小的莫来石瓷。

The research shows the completive temperature of mullitization and the increment of mullite at different temperature range varies between the calcined bauxite and fused corundum which exist with kyanite.

研究表明兰晶石和矾土熟料与和电熔刚玉共存时材料中莫来石化完成温度和不同温度阶段莫来石的增量不同；