The SEM observation disp-played that the LiNiyCo 0.1-yMn 1.9 O 4 samples have lower agglomeration degree and smaller particle size.

掺杂型 LiNiyCo0 .1-yMn1.9O4样品具有更好的分散度和小的粒径.

Therefore, the SEM-EDXA technique provides quantitative information of lignin distribution with relatively high accuracy.

因此, SEM -EDXA 技术以较高的准确度提供了定量测定木素分布的信息.

The formation and microstructure of intermetallic surfacing layers acquired by light beam heating Ni and Al mixed powder were investigated by means of X-ray diffraction, SEM, EDXS and microhardness.

采用X射线衍射、SEM、EDXS及显微硬度等方法，研究了光束堆焊Ni，Al混合粉末制备的金属间化合物涂层的成形和微观组织特征。

The structure and morphological feature of EACT were analyzed using SEM, TGA, XRD and FTIR. The results show that the modified chitosan is more stable and has internal porous structure, enhancing the adsorption performance.

采用SEM、TGA、XRD、FTIR等对EACT进行了结构和形貌分析，结果表明：改性后的壳聚糖性质更稳定，其内部大量的孔洞和褶皱增强了其吸附性能。

The profile of metal ions in Masson pinewood is researched by means of SEM EDAX and atomic absorption spectrometer. The content and retentivity of metal ions in unbleached KP AQ pulp of pinewood are studied.

用扫描电镜能谱仪（SEM EDAX）及原子吸收光谱仪研究了马尾松的金属离子分布及马尾松硫酸盐蒽醌（KP AQ）法未漂浆中金属离子的分布及滞留性能。

The microstructure changes of pearlitic eutectoid steel induced by cold rolling were investigated by using SEM, TEM and XRD etc.

用SEM、TEM及XRD等方法研究了共析钢中珠光体经40%-90%的冷轧变形后所产生的显徽组织变化。

Evaluation of Regional Tourism Competition Basc on SEM

基于结构方程模型的区域旅游产业竞争力评价

TEM and SEM analysis showed that the phase structure of AEMS and AOMS were co-continue structure and the toughening machenism was severe shear yielding when the blends reached their highest notched Izod impact strength.

TEM和SEM分析表明，缺口冲击强度达到最高值的AEMS和AOMS，其相结构为近连续相结构，增韧机理为剪切屈服机理。

The hydration products and microstructure of Class G oil_well cement and YLD sealant pastes cured under the conditions of the simulated temperature and pressure at the bottom of oil_well were investigated with XRD, TG and SEM-EDS.

采用XRD，TG和SEM-EDS等研究了在模拟油井深处温度、压力条件下养护的G级油井水泥和YLD型堵漏剂浆体的水化产物和显微结构。

Through the experimental means such as LM, SEM, TEM and XRT, the paper determines the principal causes which result in the hole cracks of gear hob.

通过LM，SEM，TEM和XRT等实验手段，确定了裂纹产生的主要原因。

It is found that PMB are spherical particles in μ m scale by SEM.

扫描电镜测度表明PMB在水基液中为均匀分散的微米球形微粒。

The process of Fish-eye Flake formation in welding seams of 16 Mng steel is investigated by means of SEM, EDX, IMA, SIMS reflectoscope and X-ray flaw detection as well as metallography technique.

运用扫描电镜、x射线能谱仪、离子探针、超声波探伤仪及x射线探伤、金相技术等多种手段对16M ng钢焊缝中鱼眼白点的形成过程作了综合研究。

The selection of bath components and plating parameters was described in detail, fine greyish white electrodeposits were obtained which were analyzed by means of SEM and XPS with results that nickel-lanthanum-phosphorus alloy electrodeposits were obtained.

详细介绍了镀液各个组分及工艺条件的选择，获得灰白色、细致的合金镀层。对所得的镀层进行SEM观察和XPS分析，结果表明所得镀层为Ni－La－P合金。

It is observed by SEM that there are slits on both TCF and JCF's surfaces, and cross section of TCF is kidney rather than round.

SEM观察表明，TCF及JCF表面都有沟槽，但TCF横断面呈腰子形非圆形；

Electron mirror phenomenon in scanning electron microscopy ( SEM ), resulting from non-conducting samples, was observed.

观察 非 导电样品在扫描电镜 ( SEM ) 中产生的电子镜现象.

SEM indicates that the shape of multi-metal phase appears to be island-like and distributes in continuous gradient clouds.

SEM形貌表明多金属相形貌为小岛状，成连续梯度云状分布。

The general characteristics of leaf epidermis of six Colocasia species under SEM shows that they have some differences in crest, epidermis appendent, stomata and the two poles of guard cell having thicken with "T" type or not, etc.

2.6种芋属植物叶表面的电镜扫描特征存在一定的差异，这些差异主要表现在叶片表面纹饰、表皮细胞的附属特征、气孔特征、保卫细胞两极是否T型加厚等方面。

SEM results showed that the surface roughness of HNCS increased and a large number of adsorption pores appeared. The specific surface area of HNCS reached 7.14 m2/ g and hydrophilic functional groups were reduced. The cellulose content was increased with the decrease of lignin content.

SEM分析发现：改性14h后的玉米秸秆表面更加粗糙，且出现大量的吸附孔隙；比表面积为7.14m2/g，表面亲水性官能团减少，纤维素含量增加而木质素含量减少。

Compared the results of qualitative analysis and of quantitative analysis, the result show that the program and methods using to process and analyze the SEM images of gypsum board and GPB is feasible and exact.

图像处理的定量分析结果进一步验证了定性分析结结论，结果证明应用上述方法和程序设计对石膏及石膏刨花板细观结构SEM图像的处理分析是可行的、有效的。

Ac-cording to the above test results and SEM observation, it seems that the durability of vinylon fibre in cement matrix is satisfactory.

上述试验结果与扫描电镜观察均证明，维纶纤维在水泥基材中有良好的耐久性。