steel的例句大全

Study on Characteristic of Thermal Fatigue Cracking Damage of Wheel Casting Steel

车轮铸钢热疲劳裂纹损伤行为研究

Corrosion Fatigue Cracking of In-service 4340 Steel Super High Pressure Pipe

在役4340钢超高压管的腐蚀疲劳开裂

Study on Hydrogen Induced Delayed Cracking of High Alloy Steel in Carbonitriding Process

高合金钢碳氮共渗氢致开裂的研究

The experimental results show that steel fiber reinforced self-stressing concrete can significantly increase the cracking load of penstock.

试验结果表明，钢纤维自应力混凝土能够明显地提高压力管道的抗裂承载力。

With increasing corrosion time the impact toughness of high Mn steel obviously decreased. The major mechanism was effect of the caustic embrittlement cracking.

随着热强碱腐蚀时间的延长，高锰钢的冲击韧度明显降低，碱脆开裂是造成高锰钢冲击韧度下降的主要原因。

With an increase of the chromium content in the cast steel, active dissolving corrosion increased, however, tendency of caustic embrittlement cracking decreased.

随着钢中含铬量的增加，试验材料的活性溶解腐蚀失重增大，但碱脆开裂的倾向减少。

Numerical simulation of slit type cracking test for 9% Ni steel

9%Ni钢斜Y形坡口裂纹试验的数值模拟

The fixed pulley is rotated by a cranking bar to wind the steel cable, a spare tire can be lifted, and the spare tire can be put down stably by rotating in reversal the cranking bar.

使用摇把转动定滑轮圈绕钢丝索，即可提升备胎，反转摇把即可平稳降下备胎。

Mechanism Analysis of the Crevice Corrosion of Liquid Chlorine Steel Cylinders and Protection Methods

液氯钢瓶缝隙腐蚀的机理分析及防范措施

Crevice Corrosion of Stainless Steel Seal Surface in Acetic Acid and Countermeasures

不锈钢密封面在醋酸中的缝隙腐蚀及对策

The phenomenon of longitudinal fission seldom occurred during the process of tube plug drawing mill compared with empty-sunken steel tube. The problem which seldom cause transverse fissure in form of partial failure owing to uniform distribution of axial stress in cross section.

与空拔相比较，在短芯棒拔制过程中，纵裂现象一般不会发生，由于钢管轴向应力在横截面上分布均匀，一般也不会出现以局部破坏形式出现的横裂现象。

According to the section temperature field distribution of the the whole heating process, derived the normal cross section ultimate flexural bearing capacity calculation formula of the simply supported prestressed steel reinforced concrete beam under high temperature.

3根据升温全过程构件截面温度场的分布，推导高温下预应力型钢混凝土简支梁的正截面极限抗弯承载力计算公式。

The calculating method for the strength of normal cross section of double steel-concrete composite continuous beam is researched, and some important conclusions are as followings: The calculating method for normal section strength of double composite beam is mainly researched in this dissertation.

本文对钢-混凝土双面组合连续梁的正截面强度计算方法进行研究，主要内容包括：（1）对钢-混凝土双面组合梁的正截面强度计算方法进行了研究。

Structural behaviors of the connections between concrete filled square tubular column and steel beam have been studied by the tensile tests of cruciform joint models with inner diaphragm.

本文通过对带内隔板的十字形连接节点的拉伸试验，研究了方钢管混凝土柱与钢梁连接的结构性能。

Effect of Heat Treatment on High-temperature Wearing Character of WC/ Steel Composite Material

热处理对WC/钢复合材料高温磨损特性的影响

Ordering Domain in High Purity Steel Containing Copper

含铜高纯钢中的有序畴

However, Wang Shiren, a government adviser, said this figure included new-built concrete and steel shopping centres decorated in a style that fitted the image of the street.

然而，担任政府顾问的王世仁表示，这一数据包括新建钢混结构购物中心，它们的装修风格都符合前门大街的风貌。

Application of High Alloy Steel on Wearing Parts of Slurry Pump

高合金钢在渣浆泵过流件上的应用

The Application of Cold Set Resin Sand in the Production of Ductile Iron and Steel Casting

冷硬树脂砂在球墨铸铁和铸钢件上的应用

Effect of Tempering Temperature on Wearing Resistance of High Vanadium High Speed Steel

克鲁普铬钼钒高速钢回火温度对高钒高速钢耐磨性的影响