Characteristics of internal friction and modulus associated with non-equilibrium diffusion-type phase transformation in eutectoid Al-Zn alloy

A Study of m-c-δ( or m-k-δ) Relations of Superplastic Zn-22% Al Eutectoid Alloy

Zn-22%Al合金超塑性的m-C-δ（或m-k-δ）关系的研究

Usually, excellent Superplasticity of Zn-Al eutectoid alloy could be obtained by pre-deformation ( rolling or forging).

锌铝共析合金具有良好的超塑性，但通常需要经过预变形（轧制或锻压）来得到。

The Study of Superplastic Mechanism of Zn-Al Eutectoid Alloy

Zn－Al共析合金室温超塑性变形机理

It was found that the superplasticity was also obtained directly by superplastic treatment of the cast Zn-Al eutectoid alloy.

研究指出，直接由铸造的锌铝共析合金进行超塑性处理，也可以得到超塑性。

Superplastic Treatment and Application of Cast Zn-Al Eutectoid Alloy

铸造锌铝共析合金的超塑性处理及应用

In this paper The hardness of grey iron is related to the amount and fineness of pearlite in the matrix, and is effected to a great extent by the amount of primary austenite and its eutectoid structure.

结果表明，灰铸铁的硬度不仅与基体中珠光体的含量和细化程度有关，而且在很大程度上还取决于铸铁结晶过程中初生奥氏体量及其共析转变的结果。

Zn-Al Eutectoid Structure Formed by Hot Compression

热压法获得Zn-Al共析组织的研究

Results The melting point of the lidocaine-dodecanol binary eutectic system was markedly lower than that of pure lidocaine.

结果利多卡因-月桂醇二元共熔混合物的熔点明显比利多卡因低。

Surfactants Improving the Dispersion of RDX in AN-EDD Eutectic System

表面活性剂改善RDX在EA低共熔物体系中的分散性研究

The Binary Phase Diagram and Eutectic System for DNTF/ PETN

DNTF/PETN体系的二元相图及低共熔物

Influence of sample thickness on the morphology of eutectic system

试样厚度对共晶组织形态的影响

Analysis has been carried out for two kinds of eutectic system with different morphology.

对两种不同形态的共晶组织进行了分析。

At the same time, the addition of aluminum to obtain another eutectic structure which is fine and disperse.

与此同时，铝的加入，获得了细密、弥散的另一共晶组织。

Investigation on the pseudo eutectic structure formed by solid diffusion of Zn powder and Al powder

Zn粉和Al粉固相扩散形成共晶类组织的研究

Study shows that quenched boron eutectic structure possesses the excellent wear abrasion property.

研究表明：硼共晶组织经淬火后，具有优良的抗磨粒磨损性能。

Eutectic Structure of Binary Mg Li Alloy During Directional Solidification

定向凝固条件下二元Mg-Li合金共晶组织的研究

The percentage elongation is affected mainly by the morphology of eutectic structure;

伸长率主要受共晶组织形态影响；

Appreciation of Crystal On the Mechanism of Eutectic Structure

论共晶结构的机理

When the pulling rates was low as 1 mm/ min, three-phase eutectic structure was observed and characteristic of directional solidification could be found in longitudinal section.

当下拉速率为1mm/min时，合金组织呈现三相共晶结构，纵截面有定向凝固趋势。

According to the results of DSC and microstructure analysis, the more Al content, the higher melting point of the alloy, but the more α phase dendrites, the less eutectic cementite.

从差示扫描量热分析和显微组织得出：随含铝量的增加，合金的熔点提高，α相枝晶增多，晶间的共晶体减少。