The wear mechanism of original WC-Ni cemented carbide during the wear process is abrasive wear with the main characteristics of plastic deformation of Ni binder phase and fall-out of WC grains, and wear resistance depends on the hardness of cemented carbide.

The erosion mechanism at 90 degrees includes block exfoliation, the plastic deformation of binder phase and the extrusion of the carbides, meanwhile, the brittle fracture character has also been observed with a speed of 420 meters per second.

90°冲蚀机制包括块状剥落，粘结相的塑性变形和碳化物的挤出，420m/s冲蚀的粘结相还表现出了脆性断裂的特点，块状剥落是质量磨损率升高的主因。

Due to the existence of surface tension, plastic film was binder together and so difficult to separate when it was compressed or heated in accumulation and bound volumes.

塑料薄膜在堆积及缠卷时，由于表面张力的存在，当受压或受热时，容易使塑料薄膜黏结在一起，不易分离，甚至无法使用。

The principle and characteristics of magnet injection molding are explained and its key technologies are analysed from magnetic particulate, plastic binder and mold, process.

并且在磁性颗粒塑料粘结剂、模具、工艺等方面分析了该工艺的关键技术。

Study on the New Producing Technique and Curing Mechanism of CO_2-Cured Phenolic Resin Binder

新型CO2硬化酚醛树脂粘结剂制备技术及硬化机理的研究

Study of synthesizing phenolic resin binder by two-step technology

二步法合成酚醛树脂结合剂的研究

Study on New Thermosetting Inorganic Resin Binder for Moulds and Cores

一种新的环保型热硬化无机高聚物铸造粘结剂研究

Research on Component and Cure Mechanism of CO_2 Cure Phenolic Resin Binder

CO2固化碱性酚醛树脂粘结剂的组成及固化机理研究

Preparation of a higher strength phenolic resin binder for casting

一种高强度铸造酚醛树脂的研制

The paper introduces good quality and multiple-use complex epoxy resin binder and its application in anti-corrosion coating of chemical storage tanks.

本文主要阐述了性能优良、应用广泛的复合型环氧树脂粘合剂，在化工贮罐、防腐涂层的工艺和方法。

The survey and analysis show that when the rut depth is deeper ( more than 60 mm), the greater deformation would be found both in wearing course and binder course, and the compression deformation ratio of binder course is higher than that of wearing course.

测量分析结果表明，车辙深度较深（大于60mm）时，上、下面层均发生了较大的变形，且下面层的压缩变形率大于上面层；

While, when the rut depth is lower ( less than 40 mm), the compression deformation ratio of binder course is lower than that of wearing course.

当车辙深度较浅（小于40mm）时，下面层的压缩变形率小于上面层。

Research and evaluation of pavement performance for ATB binder course

ATB联结层的路用性能研究与评价

By means of the concrete numerical results, properties of the axle bush, the binder bolt and the connecting tooth are discussed and a feasible simplified model is given.

通过具体的数值结果，分析了瓦、螺栓及齿的工作状态并讨论了可行的简化方案。

Strength and fatigue in high strength binder bolt

高强度紧固件中的强度与疲劳问题

Following burnout of the organic binder, the boards are white in color.

有机粘合剂燃尽后，板材的颜色为白色。

Molecular structure mould and selecting criterion of organic binder for iron ore pellet

铁矿球团有机粘结剂的分子构型及选择判据

Improving strength of iron ore pellet containing organic binder by microwave heating

微波加热提高有机粘结剂铁矿球团的强度

Strength tests of high coal pellets with organic binder

有机物粘结的高配煤球团的强度试验

Study and choice of organic binder for iron ore pellets containing carbon

竖炉型含碳球团有机粘结剂的选择与应用

Study on a Water soluble Organic Binder Sand Cured by Microwave Energy

微波固化水溶性有机粘结剂砂的研究