Specifications Temperature: 173K 1073K continuously adjustable, accuracy ± 0.5 2K, Pressure: atmosphere to 10 MPa, Vacuum: 10 6 torr, Phases: gas solid and liquid.

No,. 200 torr at the same temperature.

不是，25。200torr，在相同的温度下。

The vacuum box is outside of the optical box, can keep good vacuum at a level of 10-6 Torr. The vacuum box, vacuum pump and a refrigerator are composed of the cooling system of the camera.

光学箱外部是真空箱，是整个系统的机械支撑，保证良好的真空密封性能，和真空泵、冷冻机一起构成了相机的致冷系统。

The gas "pressure window" for building a hot electron ring is ( 0.4-1.2)× 10 (-5) Torr, as the gyrotron output is about 30 kW.

在回旋管输出30kW功率的条件下，适于建立热电子环的气体压力窗为（0.4&1.2）×10~（-5）Torr。

It shows that for obtaining strong He ⅱ ( 303.8 A) resonance radiation, which is most useful for ultraviolet photoelectron spectroscopy ( UPS) study, the He pressure should be lower than 0.1 torr.

由于HeⅡ（303.8）共振辐射对光电子谱研究最为有用，实验表明为了获得强的HeⅡ（303.8）线，He的工作气压应小于0.1乇。

The degree of vacuum during condensation is in the order of 10-5 Torr.

凝聚时的真空度为10~（-θ）乇量级。

Titanium films are deposited on Si wafers by electron-beam evaporation in vacuum, the base pressure of the system is 10-7 Torr. Solid phase reaction results through rapid thermal annealing.

钛膜在10~（-7）Torr真空中用电子束蒸发沉积在硅单晶片上，以快速热退火方式进行团相反应。

The paper describes a special equipment for vacuum friction test, and presents f-v test curves for combinations of PTFE-granite, PTFE-chromium plating steel and PTFE-steel ball in a vacuum of 10-3 Torr.

本文描述了一台专用的真空摩擦试验装置，并给出了真空度为10~（-3）托下，PTFE-花岗石、PTFE镀铬铜和PTFE钢球三种摩擦副材料的f-v实验曲线；

Youth is hotheaded, torr, but these two are good boys!

年轻就是冲动，托尔，可是这两个都是好孩子！

Antimicrobial Activity of the Extracts from Fraxinus velutina Torr Fruits

绒毛白蜡果实提取物的抑菌作用研究

During growth, the substrate is kept at room temperature and the oxygen partial pressure is 3 × 10-6 Torr.

生长时衬底温度为室温，气压为3×10-6Torr。

In the processes of reduction of Zinc oxide with carbon, the gasification reaction of carbon is the controlling step and the rate of reduction does not appear the upmost value in the range of 0.5-76 Torr.

在碳还原氧化锌的过程中，碳的气化反应是控制步骤，在0.5&10020.8Pa范围还原速率未出现极大值。

In helium gas of 37 Torr, particles with diameter of 100A were obtained. X-ray diffraction presents the pattern analogous to amorphous state.

在37乇的氦气气氛下，获得直径为100A的超微粒子，色泽乌黑，具有类似非晶的衍射花样。

The diamond nucleation and growth on Si substrate by hot filament chemical vapor deposition ( HFCVD) at the low temperature (~ 550 ℃) and low pressure (~ 7 Torr) were studied.

用热丝化学气相沉积方法研究了低温（~550℃）和低反应气压（~7Torr）下硅片上金刚石膜的成核和生长。

In the pressure range of 6-12 Torr, the relative standard deviations of relative intensities of most elements are in the range of 0.5%-2% at different powers except for 5 W.

在气压6~12Torr范围内，除5W外功率变化对大多数元素相对强度稳定性影响较小，相对标准偏差介于0·5%~2%。

Three types of ion gauges with tube electron multiplier are developed. It intends to solve the low pressure measurements up to 10~ (-14) torr.

研制成功了三种结构的具有管型电子倍增器的电离规，企图解决低到10~（-14）托的压强测量问题。

The rate of reduction of zinc oxide with carbon monoxide exhibits the upmost value at 22-24 Torr.

一氧化碳还原氧化锌的速率在（22&24）×133.3Pa出现极大值。

The water temperature in the tube has been kept at 95 × for 6000 hrs while the pressure in the vacuum jacket was lower than 5 × 10-5 Torr, it may be considered that the collector tube has long vacuum life time.

集热管内水温保持在95℃，经6000小时后真空套管中压强仍低于5×10~（-5）托，表明本集热管有长的真空寿命。

Ethyl bromide or iodide at 20 torr was irradiated by a TEA CO2 laser. The reaction products were identified by means of infrared spectrometry, gas chromatography and CW CO2 laser photoacoustic spectroscopy.

~20托溴乙烷或碘乙烷用TEA CO2激光辐照，其产物用红外光谱、气相色谱和CW CO2激光光声光谱检测。

The adhesion is better when the pressure is 30 Torr.

沉积气压为30Torr，薄膜结合强度较好。

The measurement of the total emissivity of a solid surface in the black cavity which is immersed in liquid nitrogen and under high vacuum ( 10-6 torr) by steady caloric method is described.

本文提出了一个真空度为10~（-6）毫米汞柱，黑体腔四周浸泡在液氮中的固体的表面热辐射率的测定方法。